Creality Hyper PLA Yellow is a 1.75 mm, 1 kg high-speed PLA filament for FDM printing, with ±0.03 mm diameter, a 190-230 °C nozzle range, a 25-60 °C heated bed, and speeds up to 600 mm/s.
For any questions about this item, availability, or delivery times, please contact us at 22 270068
Creality Hyper PLA Yellow is a 1.75 mm high-speed PLA filament on a 1 kg spool. Official Creality listings identify Yellow as MPN 3301010379, with high fluidity and fast cooling for print speeds up to 600 mm/s.
Verified settings are a 190-230 °C nozzle range and a 25-60 °C heated bed. Creality specifies 1.75 ± 0.03 mm diameter and low shrinkage versus ABS. This paper-spool Hyper PLA is made for everyday and high-speed FDM; RFID plastic-spool Hyper PLA is recommended for Creality CFS.
- Material: PLA
- Diameter: 1.75 mm
- Net weight: 1 kg
- Color: Yellow
- Recommended nozzle temperature: 190-230 °C
- Recommended bed temperature: 25-60 °C
| Brand | Creality |
| Product Type | PLA Filament |
| MPN | 3301010379 |
| EAN | 6971636401094 |
| Material | PLA |
| Color | Yellow |
| Diameter | 1.75 mm |
| Diameter Tolerance | ±0.03 mm |
| Net Weight | 1 kg |
| Recommended Nozzle Temperature | 190-230 °C |
| Recommended Bed Temperature | 25-60 °C |
| Recommended Print Speed | 30-600 mm/s |
| Cooling Fan | 100% |
| Density | 1.24 ± 0.1 g/cm³ at 21.5 °C |
| Glass Transition Temperature | 62 °C |
| Vicat Softening Temperature | 62.3 ± 0.5 °C |
| Tensile Strength (X-Y) | 52.99 MPa |
| Tensile Modulus (X-Y) | 1146.06 MPa |
| Elongation at Break (X-Y) | 6.3% |
| Bending Strength (X-Y) | 92.38 MPa |
| Flexural Modulus (X-Y) | 2490.17 MPa |
| Charpy Impact Strength | 8.83 kJ/m² |
| Spool Type | Paper spool |
| Printing Technology | FDM / FFF |
| Surface Finish | Standard |
| Packing Size | 210 x 210 x 70 mm |
| Gross Weight | 1.29 kg |